Stock Thickness: 0.4-20.0mm
Production thickness: 8.0-120mm
Width: 1000mm, 1219mm, 1250mm, 1500mm, 2000mm,or required
Length: 2000mm, 2438mm, 2500mm, 3000mm, 6000mm,or required
Grade:
200 series: 201,202
300 series: 301,304,304L,304H,309,309S,310S,316L,316Ti,321,321H,330
400 series: 409,409l,410,420J1,420J2,430,436,439,440A/B/C
Duplex: 329,2205,2507,904L,2304
Surface: No.1, 1D, 2D, 2B, NO.4/4K/hairline, satin, 6k, BA, mirror/8K
Standard: ASTM A240, ASME SA240, JIS G 4304, EN 10088-2.
Chanson Metals have thousands tons stock of stainless steel sheet and plate with various size and grade,mainly include austenitic stainless steel sheet & plate, martens stainless steel sheet & plate (including precipitation hardened stainless steel sheet & platel), ferritic stainless steel sheet & plate, and duplex stainless steel sheet & plate.
Technique
Cold Rolled,Hot Rolled
Width
1000mm,1219mm,125mm0,1500mm,2000mm,or required
Length
2000mm, 2438mm,2500mm,3000mm,6000mm,or required
Standard
ASTM,AISI,SUS,JIS,EN,DIN,GB,ASME,ETC
Brand
Chanson,TISCO,BAOSTEEL,POSCO,JISCO,LISCO
Application
kitchware,door,decoration,elevator,water tank,etc
Incoterm
EXW,FOB,CNF,CIF,CFR
Delivery
7 to 15 days,depends on the quantity
Chemical Analysis:
| Grade | UNS | Chemical Component % | ||||||||||
| C | Mn | P | S | Si | Cr | Ni | Mo | N | Ti | Other | ||
| 201 | S20100 | 0.15 | 5.50-7.50 | 0.06 | 0.03 | 1.00 | 16.0-18.0 | 3.50-5.50 | 0.25 | |||
| 202 | S20200 | 0.15 | 7.50-10.0 | 0.06 | 0.03 | 1.00 | 17.0-19.0 | 4.0-6.0 | 0.25 | |||
| 301 | S30100 | 0.15 | 2.00 | 0.045 | 0.03 | 1.00 | 16.0-18.0 | 6.0-8.0 | - | 0.10 | - | |
| 304 | S30400 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 18.00-20.00 | 8.0-10.5 | - | 0.10 | - | |
| 304L | S30403 | 0.03 | 2.00 | 0.045 | 0.03 | 0.75 | 18.00-20.00 | 8.0-12.0 | - | 0.10 | - | |
| 304H | S30409 | 0.04~0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 18.00-20.00 | 8.0-10.5 | - | - | - | |
| S30815 | 0.05-0.10 | 0.80 | 0.04 | 0.03 | 1.4-2.00 | 20.0-22.0 | 10.0-12.0 | - | 0.14-0.20 | - | Ce 0.03-0.08 | |
| 309S | S30908 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 22.00-24.00 | 12.00-15.00 | - | - | - | - |
| 309H | S30909 | 0.04~0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 22.00-24.00 | 12.00-15.00 | - | - | - | - |
| 310S | S31008 | 0.08 | 2.00 | 0.045 | 0.03 | 1.50 | 24.00-26.00 | 19.00-22.00 | - | - | - | - |
| 310H | S31009 | 0.04~0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 24.00-26.00 | 19.00-22.00 | - | - | - | - |
| S31254 | 0.02 | 1.00 | 0.03 | 0.01 | 0.80 | 19.5-20.5 | 17.5-18.5 | 6.0-6.5 | 0.18-0.22 | - | Cu: 0.50-1.00 | |
| 316 | S31600 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.0-14.0 | 2.00-3.00 | 0.10 | - | - |
| 316L | S31603 | 0.03 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.0-14.0 | 2.00-3.00 | 0.10 | - | - |
| 316H | S31609 | 0.04~0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.0-14.0 | 2.00-3.00 | - | - | - |
| 316Ti | S31635 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 16.00-18.00 | 10.0-14.0 | 2.00-3.00 | 0.10 | 5(C+N)-0.7 | Ti5(C+N)-0.7 |
| 317 | S31700 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 18.00-20.00 | 11.0-15.0 | 3.0-4.0 | 0.10 | - | - |
| 317L | S31703 | 0.03 | 2.00 | 0.045 | 0.03 | 0.75 | 18.00-20.00 | 11.0-15.0 | 3.0-4.0 | 0.10 | - | - |
| 321 | S32100 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 17.00-19.00 | 9.00-12.00 | - | 0.10 | 5(C+N)-0.7 | Ti5(C+N)-0.7 |
| 321H | S32109 | 0.04~0.10 | 2.00 | 0.045 | 0.03 | 0.75 | 17.00-19.00 | 9.00-12.00 | - | - | 4(C+N)-0.6 | Ti4(C+N)-0.6 |
| S32654 | 0.02 | 2.0-4.0 | 0.03 | 0.005 | 0.5 | 24.0-25.0 | 21.0-23.0 | 7.0-8.0 | 0.45-0.55 | - | Cu: 0.30-0.60 | |
| 347 | S34700 | 0.08 | 2.00 | 0.045 | 0.03 | 0.75 | 17.00-19.00 | 9.00-13.00 | - | - | - | Nb:10C-1.0 |
| 409 | S40900 | 0.03 | 1.00 | 0.04 | 0.02 | 1.00 | 10.50-11.70 | 0.5 | - | 0.03 | 6(C+N)-0.5 | Nb: 0.17 |
| 410 | S41000 | 0.08~0.15 | 1.00 | 0.04 | 0.03 | 1.00 | 11.50-13.50 | 0.75 | - | - | - | - |
| 410S | S41008 | 0.08 | 1.00 | 0.04 | 0.03 | 1.00 | 11.50-13.50 | 0.75 | - | - | - | - |
| 420 | S42000 | Min 0.15 | 1.00 | 0.04 | 0.03 | 1.00 | 12.0-14.0 | 0.75 | 0.50 | - | - | - |
| SUS420J2 | 0.16-0.25 | 1.00 | 0.04 | 0.03 | 1.00 | 12.0-14.0 | - | - | - | - | - | |
| 429 | S42900 | 0.12 | 1.00 | 0.04 | 0.03 | 1.00 | 14.0-16.0 | - | 0.75-1.25 | 0.02 | - | Nb: 3C+0.3~1.00 |
| 430 | S43000 | 0.12 | 1.00 | 0.04 | 0.03 | 1.00 | 16.0-18.0 | 0.75 | - | - | - | - |
| 431 | S43100 | 0.2 | 1.00 | 0.04 | 0.03 | 1.00 | 15.0-17.0 | 1.25-2.50 | - | - | - | - |
| 434 | S43400 | 0.12 | 1.00 | 0.045 | 0.03 | 1.00 | 16.0-18.0 | - | 0.75-1.25 | - | - | - |
| 436 | S43600 | 0.12 | 1.00 | 0.045 | 0.03 | 1.00 | 16.0-18.0 | - | 0.75-1.25 | - | - | Nb: 5C-0.80 |
| 439 | S43035 | 0.03 | 1.00 | 0.04 | 0.015 | 1.00 | 17.50-18.50 | - | - | - | 0.10-0.60 | Nb: Min (0.3+3C) |
| 440A | 0.60-0.75 | 1.00 | 0.04 | 0.03 | 1.00 | 16.0-18.0 | - | 0.75 | - | - | - | |
| 440B | 0.75-0.95 | 1.00 | 0.04 | 0.03 | 1.00 | 16.0-18.0 | - | 0.75 | - | - | - | |
| 440C | 0.95-1.20 | 1.00 | 0.04 | 0.03 | 1.00 | 16.0-18.0 | - | 0.75 | - | - | - | |
| 441 | S44100 | 0.03 | 1.00 | 0.04 | 0.015 | 1.00 | 17.50-18.50 | - | - | 0.03 | 0.1-0.6 | Nb: 3C+0.3~1.0 |
| 444 | S44400 | 0.025 | 1.00 | 0.045 | 0.03 | 1.00 | 17.5-19.5 | 1.00 | 1.75-2.50 | 0.035 | Ti+Nb:[0.20+4(C+N)]-0.80 | |
Surface Characteristics and Application:
Surface
Characteristics and application
1D - No. 1
Hot rolled, metallic pure, annealed, pickled and heat treated. The most common hot rolled finish. A non reflective, rough surface. Not normally used for decorative applications
2D
Matt, cold rolled, annealed, pickled. This material is cold rolled followed by softening and de-scaling. The effect of cold rolling the material is to produce a smoother, less pitted surface. The surface is not only smooth but of matt grain appearance. Used where a better surface is required or subsequent processing/ finishing is necessary.
2B
Matt glossy, cold rolled, annealed, pickled, skinpassed. This is the general purpose, cold rolled finish and it is suitable for a wide range of applications where stainless steel is specified. It is also suitable for a wide range of subsequent polishing processes such as satin finishing and grinding..
2R - BA
Mirror glossy, bright annealed. The effect of annealing without the presence of oxygen is to produce a reflective surface on the stainless steel and it is often used in preference to a 2B finish where reflectivity is important, such as catering equipment. The very smooth surface also makes this surface highly suitable for further finishing processes such as mirror polishing and chrome plating.
2G- 4N
No. 4 Finish is characterized by short, parallel polishing lines, which extend uniformly along the length of the coil. No 4 finish gives low gloss and best apparent flatness of panels. For fabricators, the No 4 finish is directional, allowing easy matching of surfaces and refinishing of welds. For end users, the surface can be repaired to remove any service damage. No 4 finish is duller than the other common finishes, 2B and BA and is generally used where lower reflectivity or gloss is required and where welds and other fabrication marks are to be refinished to match the original surface. This is not possible with 2B and difficult with BA.
Mirror - 8K
#8 mirror-polished is the top quality surface finish. Surface blemishes are eliminated by the complete finishing process to achieve a mirrorlike appearance. Such fine quality can be achieved without any extra finishing or coating materials being added. the characteristics of high reflectivity and a lustrous shine allow them to complete any kind of architectural or interior decoration.
Chanson Metals provide:
1. Professional packing team guarantee goods arrive in good condition (anti-wet paper +wooden pallet)
2. Professional loading team avoid package damage
3. Goods label with traceable batch number and shipping information
4. Leveling machine and polishing machine makes various size and surface available.
5. Varous sizes and materials stock more than 1000 tons